<sec><title>Aim:</title><p> To assess the effect of different torque values on cyclic fatigue resistance of K3 rotary nickel-titanium (NiTi) files.</p></sec><sec><title>Methods:</title><p> Eighty K3 files, size 25 mm, taper 0.04 were divided in 4 groups according to different torques (0.5, 1, 2 and 6 Ncm) and were submitted to a cyclic fatigue test. This test was performed with a device that allowed the file to rotate inside a stainless steel artificial curved canal, simulating the pecking motion. Files rotated until fracture occurred and time to failure was recorded in seconds with a stopwatch. Data were analyzed by ANOVA and Tukey tests (p<0.05).</p></sec><sec><title>Results:</title><p> All groups were compared and only the group of 6 N.cm showed statistically significant difference (p=0.0002).</p></sec><sec><title>Conclusions:</title><p> For #25.04 K3 files, the evaluated torques up to 2 N.cm had no influence on cyclic fatigue resistance. Using 6 N.cm torque value resulted in lower resistance to cyclic fatigue.</p></sec>

The aim of this study was to evaluate the penetration of a resin/polyester polymer-based material (Resilon Real Seal; SybronEndo Corp., Orange, USA) into simulated lateral canals, and the quality of obturations by different techniques. A total of 30 standardized simulated canals were divided into three groups according to the technique of obturation used: MS (McSpadden), SB (SystemB/Obtura II), and LC (Lateral Condensation). To analyze the penetration of the filling material, the simulated canals were digitalized and the images were analyzed using the Leica QWIN Pro v2.3 software. The data of the middle and apical thirds were separately submitted to analysis of variance (ANOVA), followed by the Tukey’s test for the comparison of the techniques. Results showed a significant difference (p < 0.05) between groups (LC < SB) in the middle third, and a significant difference (p < 0.05) between groups (LC < SB and MS < SB) in the apical third. To analyze the quality of the obturations, the canals were radiographed and evaluated by three examiners. The Kappa test on interexaminer agreement and the nonparametric Kruskal-Wallis test indicated no significant difference between filling techniques. It was concluded that Resilon achieves greater levels of penetration when associated with thermoplastic obturation techniques.

The aim of this study was to evaluate the quality of filling in main and lateral root canals performed with the McSpadden technique, regarding the time spent on the procedure and the type of gutta-percha employed. Fifty simulated root canals, made with six lateral canals placed two apiece in the cervical, middle and apical thirds of the root, were divided into 5 groups. Group A: McSpadden technique with conventional gutta-percha, performed with sufficient time for canal filling; Group B: McSpadden technique with conventional gutta-percha, performed in twice the mean time used in Group A; Group C: McSpadden technique with TP gutta-percha, performed with sufficient time for canal filling; Group D: McSpadden technique with TP gutta-percha, performed in twice the mean time used in Group C; Group E: lateral condensation technique. Images of the filled root canals were taken using a stereomicroscope and analyzed using the Leica QWIN Pro software for filling material flow, gutta-percha filling extension and sealer flow. Data were analyzed by analysis of variance (ANOVA) and Tukey test (p < 0.05). The best values of penetration in lateral canals in the middle third occurred in the groups where TP gutta-percha was used. However, in the apical third, group B showed the best values. Although a longer time of compactor use allows greater penetration of the filling material into the lateral canals, the presence of voids resulted in bad quality radiographic images, suggesting porosity. The best quality of filling material was observed in Group A (McSpadden technique with conventional Gutta-Percha, performed with sufficient time for root canal filling).